In oil and gas production environments, hydrogen sulfide (H2S) is often encountered. The presence of ‘wet’H2S, also known as sour-service, can result in cracking and failure of carbon and low alloy steels as well as corrosion-resistant alloys (CRA’s). Therefore testing and qualifying these materials to ISO 15156 / NACE MR0175 requirements is critical for sour-service applications.
Testing to NACE MR0175 / ISO 15156 requirements
Testing and qualification to the provisions of ISO 15156/NACE MR0175 are split into two separate categories:
- Part 2 for carbon and low alloy steels and
- Part 3 for corrosion-resistant alloy’s
Carbon and low alloy steel testing
For carbon and low alloy steels, Part 2 of the standard covers the testing and qualification requirements for sulfide stress cracking (SSC), hydrogen-induced cracking (HIC Testing), and stress-orientated hydrogen-induced cracking (SOHIC). For all of the carbon and low alloy steel cracking modes, the highest susceptibility exists at ambient temperature. Additionally, the critical environmental factors to consider are the solution pH and partial pressure of H2S.
Corrosion-resistant alloy testing
For corrosion-resistant alloys, Part 3 of the standard covers the testing and qualification for sulfide stress cracking (SSC), stress corrosion cracking (SCC), and galvanically-induced hydrogen stress cracking (GHSC). For stress corrosion cracking, the most significant susceptibility occurs at ambient or low temperatures. For stress-corrosion cracking, the highest susceptibility is usually at the maximum operating temperature or an intermediate temperature (i.e., 80 – 100 °C) in the case of duplex stainless steels. For corrosion-resistant alloys, with the exception of temperature, the critical environmental factors are the solution pH, chloride concentration, and the partial pressure of H2S.
The ÌìÃÀ´«Ã½ advantage
Element has an integrated global network of laboratories that offer the complete range of sour-service tests for the qualification of your materials to the requirements of MR0175 / ISO 15156. Testing is conducted in accordance with NACE TM0177 (SSC / SCC / GHSC), NACE TM0316 (SSC / SCC), NACE TM0284 (HIC), NACE TM0198 (SSRT) and BS8701 (Full Ring).
In addition to testing, ÌìÃÀ´«Ã½’s experts, with extensive experience of the MR0175 / ISO 15156 standard, can offer guidance and advice on the interpretation of the standard and the selection of the most appropriate test program for your application.
Contact our corrosion experts for more information.
Predicting component life with corrosion modeling
Erosion within oil and gas pipelines is a serious problem. Corrosion modeling using the Computational Fluid Dynamic method can accurately predict the location of burn-throughs.
Read MoreFracture Mechanics in Sour Service: Some Characterization Tests on SENT and SENB Specimen
This article provides better understanding of how the SENT test technique influences fracture toughness of pipelines in sour service environments.
Read MoreUnderstanding Mixed Flowing Gas Testing
Mixed flowing gas (MFG) testing is an accelerated aging test that specifically evaluates the corrosion of electrical components due to exposure to atmospheric gasses and contaminants.
Read MoreRelated Services
Sour Service Corrosion Testing
ÌìÃÀ´«Ã½ is one of a few ISO certified sour service labs in the world, providing sour service corrosion services for a variety of test types including NACE MR0175/ISO 15156.
Sulfide Stress Cracking (SSC) Testing
ÌìÃÀ´«Ã½'s SSC (Sulfide Stress Cracking) testing according the NACE TM0177/ ISO 15156 standard helps ensure sour service pipelines’ reliability and longevity.
Stress Corrosion Cracking (SCC) Testing
ÌìÃÀ´«Ã½â€™s Stress Corrosion Cracking (SCC) testing evaluates the susceptibility of metals to cracking failure under tensile stress and corrosion.
Hydrogen Induced Cracking (HIC) Testing
ÌìÃÀ´«Ã½â€™s HIC tests evaluate material susceptibility to hydrogen induced cracking in a sour environment in accordance with NACE TM0284.